PA66 CM3004-V0 日本东丽工业株式会社 pa66工程塑料物性数据 |
规格级别: | 阻燃级 | 外观颜色: | --- |
用途概述: | --- | ||
备注说明: | 类型:尼龙-66未强化,阻燃等级,非卤素。 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 吸水率 | (24小时)23°C | ASTM D-570 | 1.1 | % |
物理性能 | 比重 | --- | ASTM D-792 | 1.18 | --- |
抗燃级 | --- | UL 94 | 113 | --- | |
机械性能 | 抗拉屈股强度 | 23°C | ASTM D-638 | 850 | kg/cm2 |
抗拉断裂强度 | 23°C | ASTM D-638 | 12 | kg/cm2 | |
挠曲强度 | -40°C | ASTM D-790 | 1210 | kg/cm2 | |
挠曲模量 | -40°C | ASTM D-790 | 34500 | kg/cm2 | |
埃佐德卫声 | 无缺口1/2" 23°C | --- | 5 | kg.cm/cm | |
电气性能 | 体积电阻率 | --- | ASTM D-257 | V-0 | Ω.cm |
介电强度 | 1/8" 短时间 | ASTM D-149 | 17 | KV/mm | |
抗电弧性 | 1/8" | ASTM D-150 | 127 | --- | |
IEC导电径踪指数 | 导热率温度指表 | UL 746 | 600<= | V | |
热 性 能 | 热挠曲温度 | 4.6kg/cm2(18.6kg/cm2) | ASTM D-648 | 244 | °C |
熔点 | --- | 差示扫描测热计DSC法 | 265 | °C |
PA66 CM3006 日本东丽工业株式会社 pa66塑胶原料物性数据 |
规格级别: | --- | 外观颜色: | --- |
用途概述: | --- | ||
备注说明: | 类型:尼龙-66未强化 |
性能项目 | 试验条件[状态] | 测试方法 |
|
数据单位 | |||||
基本性能 | 吸水率 | 23℃ | ASTM D-570 |
|
% | ||||
物理性能 | 比重 | --- | ASTM D-792 |
|
--- | ||||
泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 |
|
mg/1000次 | |||||
机械性能 | IZOD冲击强度 | 23℃,无缺口1/2 | --- |
|
kg.cm/cm | ||||
IZOD冲击强度 | 23℃,无缺口1/8 | --- |
|
kg.cm/cm | |||||
洛氏硬度 | 23℃ | ASTM D-785 |
|
R | |||||
洛氏硬度 | 23℃ | ASTM D-785 |
|
--- | |||||
抗拉屈服强度 | -40℃ | ASTM D-638 |
|
Kg/cm2 | |||||
抗拉屈服强度 | 23℃ | ASTM D-638 |
|
Kg/cm2 | |||||
抗拉屈服强度 | 80℃ | ASTM D-638 |
|
Kg/cm2 | |||||
抗拉断裂强度 | 23℃ | ASTM D-638 |
|
Kg/cm2 | |||||
断裂伸长率 | 23℃ | ASTM D-638 |
|
% | |||||
挠曲强度 | -40℃ | ASTM D-790 |
|
Kg/cm2 | |||||
挠曲强度 | 23℃ | ASTM D-790 |
|
Kg/cm2 | |||||
挠曲强度 | 80℃ | ASTM D-790 |
|
Kg/cm2 | |||||
挠曲��量 | -40℃ | ASTM D-790 |
|
Kg/cm2 | |||||
挠曲模量 | 23℃ | ASTM D-790 |
|
Kg/cm2 | |||||
挠曲模量 | 80℃ | ASTM D-790 |
|
Kg/cm2 | |||||
压缩强度 | 23℃ | ASTM D-695 |
|
Kg/cm2 | |||||
抗剪强度 | 23℃ | ASTM D-732 |
|
Kg/cm2 | |||||
IZOD冲击强度 | -40℃,无缺口1/2 | --- |
|
kg.cm/cm | |||||
电气性能 | 体积电阻率 | --- | ASTM D-257 |
|
Ω.cm | ||||
介电常数 | 50HZ | ASTM D-150 |
|
--- | |||||
损耗因素 | 50Hz | ASTM D-150 |
|
--- | |||||
IEC导电径踪指数 | --- | UL 746 |
|
V | |||||
热 性 能 | UL-94抗燃级 | 1/16" | UL 94 |
|
--- | ||||
线性热膨胀系数 | --- | ASTM D-696 |
|
10-5cm/cm | |||||
热挠曲温度 | 4.6kg/cm2 | ASTM D-648 |
|
℃ | |||||
熔点 | --- | 差示扫描测热计DSC法 |
|
℃ | |||||
比热 | --- | --- |
|
Cal/g.°C | |||||
导热系数 | --- | --- |
|
Kcal/m.hr.°C |