PEI ES003E 物性

添加时间:2012-11-17 09:11

LNP* Faradex* Compound
LNP Faradex Resin All Series
LNP* Faradex* compounds provide electromagnetic and radio frequency interference (EMI/RFI) attenuation in applications from electronics to material handling. Faradex compounds can also be used in applications where electrostatic discharge (ESD) is required. Faradex* compounds provide mechanical properties, part weight and a design freedom similar to standard unfilled base resins. LNP* specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™Faradex™ Compound PEI ES003E 塑料数据

Also known as:LNP™Faradex™Compound EMI-X ES-1003 EM
Product reorder name:ES003E
LNP* Faradex* ES003E is a Polyetherimide resin containing stainless steel fibers. Characteristics of this grade are EMI/RFI Shielding.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 1070 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 1070 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 4.8 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 5 % ASTM D 638
Tensile Modulus,50mm/min 47500 kgf/cm² ASTM D 638
Flexural Modulus,1.3mm/min,50mm span 46800 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 99 MPa ISO 527
Tensile Stress,break,5mm/min 98 MPa ISO 527
Tensile Strain,yield,5mm/min 4 % ISO 527
Tensile Strain,break,5mm/min 4.3 % ISO 527
Tensile Modulus,1mm/min 4340 MPa ISO 527
Flexural Stress 155 MPa ISO 178
Flexural Modulus,2mm/min 4310 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 49 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
Multiaxial Impact 13 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 77 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 33 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 190 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 180 ASTM D 648
CTE,-30℃ to 30℃,flow 4.00E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 4.40E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 194 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 177 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.46 - ASTM D 792
Density 1.46 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.19 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.6-0.8 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.8-1 % ASTM D 955
Moisture Absorption(23℃/50% RH) 0.27 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 2.E+00-4.E+00 Ohm ASTM D 257
Source GMD,last updated:2008/08/22

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.德国巴斯夫PA66 A3HG7 含35玻纤增强