PEI GP080 物性
添加时间：2012-11-17 09:18LNP* Faradex* Compound
LNP Faradex Resin All Series
LNP* Faradex* compounds provide electromagnetic and radio frequency interference (EMI/RFI) attenuation in applications from electronics to material handling. Faradex compounds can also be used in applications where electrostatic discharge (ESD) is required. Faradex* compounds provide mechanical properties, part weight and a design freedom similar to standard unfilled base resins. LNP* specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™Faradex™ Compound PEI GP080 塑料数据
ULTEM foam is a polyetherimide based thermoplastic foam with a high strength to weight ratio with low moisture absorption. The foam also possesses excellent dielectric properties. ULTEM foam is targeted at applications where structural fire performance, radar transparency, or extreme hot or cold environments are required. ULTEM foam is thermoformable and compatible with phenolic pre-pregs. Information on processing or secondary operations is available upon request.
| MECHANICAL | Value | Unit | Standard |
| Compressive Strength perpendicular to plane | 12 | kgf/cm² | ASTM D 1621 |
| Compressive Modulus perpendicular to plane | 720 | kgf/cm² | ASTM D 1621 |
| Tensile Strength in plane | 17 | kgf/cm² | ASTM D 638 |
| Tensile Modulus in plane | 370 | kgf/cm² | ASTM D 638 |
| Shear Strength | 10 | kgf/cm² | ASTM C 273 |
| Shear Modulus | 190 | kgf/cm² | ASTM C 273 |
| Impact Strength | 0.8 | cm-kgf/cm² | ISO R179 |
| THERMAL | Value | Unit | Standard |
| Coefficient of Thermal Conductivity | 0.037 | W/m-K | ASTM C 518 |
| PHYSICAL | Value | Unit | Standard |
| Density | 0 | g/cm³ | ASTM D 1622 |
| Water Absorption | 4 | % | ASTM C 272 |
| Source GMD,last updated:2012/01/30 | |||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.PES J1000AE 空心的聚醚砜化合物,易成型