工程塑料注塑,加工,参数,物性

PEI ECL36 物性

添加时间:2012-11-20 09:11

LNP Lubricomp* High Temperature Resins Compound
Adding friction control & wear resistance
High temperature LNP Lubricomp compounds provide Improved wear resistance and lower friction by combining internal lubricants with high performance base resins. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound PEI ECL36 塑料物性

Also known as:LNP™ Lubricomp™ Compound ECL-4036
Product reorder name:ECL36
LNP* Lubricomp* ECL36 is a compound based on Polyetherimide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,break 1820 kgf/cm² ASTM D 638
Tensile Strain,break 1.7 % ASTM D 638
Flexural Stress 2350 kgf/cm² ASTM D 790
Flexural Modulus 195400 kgf/cm² ASTM D 790
Tensile Stress,break 160 MPa ISO 527
Tensile Strain,break 1.2 % ISO 527
Tensile Modulus,1mm/min 21600 MPa ISO 527
Flexural Stress 210 MPa ISO 178
Flexural Modulus 16000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 27 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
Izod Impact,unnotched 80*10*4 +23℃ 18 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
PHYSICAL Value Unit Standard
Density 1.48 g/cm³ ASTM D 792
Mold Shrinkage,flow,24 hrs(5) 0.04 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.4 % ASTM D 955
Wear Factor Washer 31 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.39 - ASTM D 3702 Modified
Static COF 0.48 - ASTM D 3702 Modified
Density 1.5 g/cm³ ISO 1183
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+01-1.E+06 Ohm ASTM D 257
Source GMD,last updated:2004/10/04
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Maximum Moisture Content 0.05 %
Melt Temperature 360-365
Front-Zone 3 Temperature 365-375
Middle-Zone 2 Temperature 355-365
Rear-Zone 1 Temperature 345-355
Mold Temperature 120-150
Back Pressure 0.3-0.7 MPa
Screw Speed 60-100 rpm
Source GMD,last updated:2004/10/04

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.