工程塑料注塑,加工,参数,物性
PEI EE004 物性表
添加时间：2012-12-28 22:18LNP STAT-KON* HIGH TEMPERATURE RESINS COMPOUND
BALANCE HIGH TEMPERATURE AND ELECTRICAL PROPERTIES
High temperature LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PEI EE004 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound EC-1004
Product reorder name:EE004
LNP* Stat-kon* EE004 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,break | 1730 | kgf/cm² | ASTM D 638 |
| Tensile Strain,break | 2 | % | ASTM D 638 |
| Flexural Stress | 2640 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 125700 | kgf/cm² | ASTM D 790 |
| Tensile Stress,break | 175 | MPa | ISO 527 |
| Tensile Strain,yield | 2 | % | ISO 527 |
| Tensile Modulus,1mm/min | 14500 | MPa | ISO 527 |
| Flexural Stress | 250 | MPa | ISO 178 |
| Flexural Modulus | 12000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 54 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,unnotched 80*10*4 +23℃ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 212 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 1.00E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 6.00E-05 | 1/℃ | ISO 11359-2 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 210 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.34 | g/cm³ | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 0.1-0.3 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.3-0.5 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 0.1-0.3 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.3-0.5 | % | ISO 294 |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Moisture Absorption(23℃ / 50% RH) | 0.2 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+02-1.E+06 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+02-1.E+06 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant,94V-0 Flame Class Rating(3)(4) | 0.5 | mm | UL 94 by SABIC-IP |
| Source GMD,last updated:2004/10/01 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120-150 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 360-365 | ℃ |
| Front-Zone 3 Temperature | 365-375 | ℃ |
| Middle-Zone 2 Temperature | 355-365 | ℃ |
| Rear-Zone 1 Temperature | 345-355 | ℃ |
| Mold Temperature | 120-150 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 60-100 | rpm |
| Source GMD,last updated:2004/10/01 | ||