快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
工程塑料注塑,加工,参数,物性
PEI EE005E 物性表
添加时间：2012-12-28 22:28LNP STAT-KON* HIGH TEMPERATURE RESINS COMPOUND
BALANCE HIGH TEMPERATURE AND ELECTRICAL PROPERTIES
High temperature LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PEI EE005E 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound EC-1005 EM
Product reorder name:EE005E
LNP STAT-KON* EE005E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,break | 2040 | kgf/cm² | ASTM D 638 |
| Tensile Strain,break | 2.1 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 125700 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 2830 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 146000 | kgf/cm² | ASTM D 790 |
| Tensile Stress,break | 194 | MPa | ISO 527 |
| Tensile Strain,break | 2.1 | % | ISO 527 |
| Tensile Modulus,1mm/min | 11700 | MPa | ISO 527 |
| Flexural Stress | 276 | MPa | ISO 178 |
| Flexural Modulus | 15010 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 45 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 106 | cm-kgf | ASTM D 3763 |
| Multiaxial Impact | 72 | cm-kgf | ISO 6603 |
| Izod Impact,unnotched 80*10*4 +23℃ | 29 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 207 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 1.90E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 2.71E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 1.92E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 2.71E-05 | 1/℃ | ISO 11359-2 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 207 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.365 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.16 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.05-0.3 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.3-0.5 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 0.1-0.3 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.3-0.5 | % | ISO 294 |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Moisture Absorption(23℃/50% RH) | 0.23 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+02-1.E+06 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+02-1.E+05 | Ohm | ASTM D 257 |
| Source GMD,last updated:2004/10/01 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120-150 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 360-365 | ℃ |
| Front-Zone 3 Temperature | 365-375 | ℃ |
| Middle-Zone 2 Temperature | 355-365 | ℃ |
| Rear-Zone 1 Temperature | 345-355 | ℃ |
| Mold Temperature | 120-150 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 60-100 | rpm |
| Source GMD,last updated:2004/10/01 | ||