工程塑料注塑,加工,参数,物性
PEI EEF42 物性表
添加时间：2012-12-28 22:38LNP STAT-KON* HIGH TEMPERATURE RESINS COMPOUND
BALANCE HIGH TEMPERATURE AND ELECTRICAL PROPERTIES
High temperature LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PEI EEF42 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound ECF-1006
Product reorder name:EEF42
LNP STAT-KON* EEF42 is a compound based on Polyetherimide resin containing Carbon Fiber, Glass Fiber. Added features of this material include: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 1940 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 1860 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 1.7 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 1.7 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 151100 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 2520 | kgf/cm² | ASTM D 790 |
| Flexural Stress,yld,1.3mm/min,50mm span | 2690 | kgf/cm² | ASTM D 790 |
| Flexural Stress,brk,1.3mm/min,50mm span | 2690 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 140700 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5mm/min | 179 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 179 | MPa | ISO 527 |
| Tensile Strain,yield,5mm/min | 1.5 | % | ISO 527 |
| Tensile Strain,break,5mm/min | 1.5 | % | ISO 527 |
| Tensile Modulus,1mm/min | 13990 | MPa | ISO 527 |
| Flexural Modulus,2mm/min | 13330 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 134 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 6 | cm-kgf/cm | ASTM D 256 |
| Multiaxial Impact | 30 | cm-kgf | ISO 6603 |
| Instrumented Impact Total Energy,23℃ | 112 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 +23℃ | 28 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 213 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 209 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 3.80E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 3.30E-05 | 1/℃ | ASTM E 831 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 214 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 210 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.48 | - | ASTM D 792 |
| Density | 1.47 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.14 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.1-0.3 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.3-0.5 | % | ASTM D 955 |
| Moisture Absorption(23℃/50% RH) | 0.22 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+03-1.E+06 | Ohm | ASTM D 257 |
| Source GMD,last updated:2011/01/06 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120-150 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 360-365 | ℃ |
| Front-Zone 3 Temperature | 365-375 | ℃ |
| Middle-Zone 2 Temperature | 355-365 | ℃ |
| Rear-Zone 1 Temperature | 345-355 | ℃ |
| Mold Temperature | 120-150 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 60-100 | rpm |
| Source GMD,last updated:2011/01/06 | ||