PET 物性表 PET GW520CS NC010数据表 工程塑胶

湘樟:PEEK - PTFE - PPE - PVDF - SBS - TPV - TPX - PA6 - PBE - SBR - PVC - PSU - SAN - PA66 - HIPS - 聚四氟乙烯

Color Stable Resins
颜色稳定的树脂

Rynite® GW520CS NC010 is a 20% glass fiber reinforced, flame retardant, color stabilized, modified polyethylene terephthalate resin.
rynite®GW520CS NC010是一个20%玻璃纤维增强,阻燃,色彩稳定,改性聚乙烯对苯二甲酸丁二酯树脂。

Property
Test Method
Units
Value
Identification
Part Marking Code
ISO 11469
 
>PET-GF20FR<
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Notched Charpy Impact Strength
Unnotched Charpy Impact Strength
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
2
kJ/m
145(21)
2.5
9000(1340)
9
30
Thermal
Deflection Temperature
1.80MPa
Melting Temperature
10/min
ISO 75-1/-2
ISO 11357-1/-3
()
()
232(450)
251(484)
Electrical
CTI
CTI M
IEC 60112
IEC 60112
V
V
200
125

Property
Test Method
Units
Value
Flammability
Flammability Classification
0.75mm
3.0mm
Glow Wire Flammability Index
0.75mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.75mm
1.5mm
3.0mm
High Amperage Arc Ignition Resistance
0.75mm
3.0mm
Hot Wire Ignition
0.75mm
3.0mm
UL94
IEC 60695-2-12
IEC 60695-2-13
UL 746A
UL 746A
arcs
s
V-2
V-2
950
960
960
900
925
925
150
150
150
150
Temperature Index
RTI, Electrical
0.75mm
3.0mm
RTI, Impact
0.75mm
3.0mm
RTI, Strength
0.75mm
3.0mm
UL 746B
UL 746B
UL 746B
140
140
140
140
140
140
Other
Density
ISO 1183
3           3
kg/m(g/cm )
1610(1.61)

Property
Test Method
Units
Value
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
 
()
()
()
h
()
%
270-300(520-570)
280(535)
130 - 140(266 - 284)
4
120(250)
<0.02

Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm unless otherwise stated.
Test temperatures are 23 unless otherwise stated.

The DuPont Oval Logo, DuPont™, The miracles of science™ and Rynite® are trademarks or registered trademarks of DuPont Company. Copyright© 2011

塑料UL