DuPont™ Hytrel®
thermoplastic polyester elastomer
Hytrel® DYM250S BK472 is a medium modulus resin suited for injection molding of Air Bag Deployment Doors. It has a nominal durometer hardness of 49D and contains fine particle size carbon black.
Property
|
Test Method
|
Units
|
Value
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
TPC-ET+PBT
>TPC-ET+PBT<
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Tensile Stress
@ 10% Strain
@ 50% Strain
Flexural Modulus
Hardness, Shore D
15s
Maximum
Brittleness Temperature
Tear Strength
Normal
Parallel
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 868
ISO 974
ISO 34-1 method B/a
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
℃(℉)
kN/m(lb/in)
|
30(4.4)
500
230(33.4)
10(1.5)
13(1.9)
250(36)
46
49
-100(-148)
90(514)
110(629)
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
50(122)
40(104)
222(432)
|
Property
|
Test Method
|
Units
|
Value
|
Thermal
Vicat Softening Temperature
10N, 50℃/h
|
ISO 306
|
℃(℉)
|
150(302)
|
Rheological
Melt Mass-Flow Rate
240℃, 2.16kg
|
ISO 1133
|
g/10 min
|
15
|
Other
Density
|
ISO 1183
|
3 3
kg/m(g/cm )
|
1160(1.16)
|
Processing - Injection Molding
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
240-250(465-480)
245(473)
45-55(115-130)
45(115)
3-4
110(230)
<0.05
|