PPA UX95672 物性

添加时间:2012-11-21 12:59

LNP Lubricomp* High Temperature Resins Compound
Adding friction control & wear resistance
High temperature LNP Lubricomp compounds provide Improved wear resistance and lower friction by combining internal lubricants with high performance base resins. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound PPA UX95672 塑料物性

Also known as:LNP™ Lubricomp™ Compound PDX-U-95672
Product reorder name:UX95672
LNP LUBRICOMP* UX95672 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,break 1660 kgf/cm² ASTM D 638
Tensile Strain,break 1.7 % ASTM D 638
Tensile Modulus,50mm/min 130000 kgf/cm² ASTM D 638
Flexural Stress 2600 kgf/cm² ASTM D 790
Flexural Modulus 114500 kgf/cm² ASTM D 790
Tensile Stress,break 132 MPa ISO 527
Tensile Strain,break 1.3 % ISO 527
Tensile Modulus,1mm/min 11480 MPa ISO 527
Flexural Stress 262 MPa ISO 178
Flexural Modulus 11330 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 64 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 5 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 41 cm-kgf ASTM D 3763
Multiaxial Impact 20 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 44 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 6 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 260 ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 255 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.46 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.28 % ASTM D 570
Density 1.46 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.33 % ISO 62
Source GMD,last updated:2004/09/30
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Maximum Moisture Content 0.15 %
Melt Temperature 320-350
Front-Zone 3 Temperature 330-345
Middle-Zone 2 Temperature 325-340
Rear-Zone 1 Temperature 315-325
Mold Temperature 50-105
Back Pressure 0.3-0.7 MPa
Screw Speed 60-100 rpm
Source GMD,last updated:2004/09/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.