PPA UFL36SXP 物性

添加时间:2012-11-21 12:59

LNP Lubricomp* High Temperature Resins Compound
Adding friction control & wear resistance
High temperature LNP Lubricomp compounds provide Improved wear resistance and lower friction by combining internal lubricants with high performance base resins. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound PPA UFL36SXP 塑料物性

Also known as:LNP™ Lubricomp™ Compound UFL-4036 HS
Product reorder name:UFL36SXP
LNP LUBRICOMP* UFL36SXP is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized.

MECHANICAL Value Unit Standard
Tensile Stress,break 2000 kgf/cm² ASTM D 638
Tensile Strain,break 2.5 % ASTM D 638
Tensile Modulus,50mm/min 126500 kgf/cm² ASTM D 638
Flexural Stress 2860 kgf/cm² ASTM D 790
Flexural Modulus 110300 kgf/cm² ASTM D 790
Tensile Stress,break 196 MPa ISO 527
Tensile Strain,break 2.5 % ISO 527
Tensile Modulus,1mm/min 9880 MPa ISO 527
Flexural Stress 285 MPa ISO 178
Flexural Modulus 11220 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 105 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 11 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 67 cm-kgf ASTM D 3763
Multiaxial Impact 26 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 70 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 12 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 259 ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 263 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.55 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.33 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.2 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.8 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.17 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.82 % ISO 294
Wear Factor Washer 18 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.59 - ASTM D 3702 Modified
Static COF 0.52 - ASTM D 3702 Modified
Density 1.55 g/cm³ ISO 1183
Source GMD,last updated:2004/09/30
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.15 %
Melt Temperature 315-330
Front-Zone 3 Temperature 325-340
Middle-Zone 2 Temperature 315-325
Rear-Zone 1 Temperature 310-320
Mold Temperature 150-170
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/09/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.