PPA UFL36AS 数据表

添加时间:2012-12-08 09:47

NP* Lubricomp* Compound
LNP Lubricomp Resin All Series
LNP* Lubricomp* compounds provide improved wear resistance and lower friction by combining engineering resins with internal lubricants. Lubricomp compounds, which can also be stiffened with glass or other fiber, can help extend product life and reduce or eliminate squeaks and other noise from moving parts. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ LUBRICOMP™ Compound PPA UFL36AS 塑料数据

Also known as:LNP™ Lubricomp™ Compound UFL-4036 A HS BK8-115
Product reorder name:UFL36AS
LNP* Lubricomp* UFL36AS is a Polyphthalamide (PPA) base resin containing Glass Fiber and PTFE. Characteristics are Heat Stabilization.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 1920 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 1920 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 1.7 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 1.7 % ASTM D 638
Tensile Modulus,50mm/min 157200 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 2460 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3mm/min,50mm span 2370 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 108000 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 192 MPa ISO 527
Tensile Stress,break,5mm/min 192 MPa ISO 527
Tensile Strain,yield,5mm/min 1.9 % ISO 527
Tensile Strain,break,5mm/min 1.9 % ISO 527
Tensile Modulus,1mm/min 12570 MPa ISO 527
Flexural Modulus,2mm/min 11290 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 72 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
Multiaxial Impact 20 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 90 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 46 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 9 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 277 ASTM D 648
CTE,-30℃ to 30℃,flow 2.10E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 4.50E-05 1/℃ ASTM D 696
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 273 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.58 - ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.15 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.2-0.4 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.8-1 % ASTM D 955
Wear Factor Washer 5 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Wear Factor Ring 0 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.48 - ASTM D 3702 Modified
Static COF 0.52 - ASTM D 3702 Modified
Density 1.57 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.25 % ISO 62
Source GMD,last updated:2008/10/07
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.15 %
Melt Temperature 315-330
Front-Zone 3 Temperature 325-340
Middle-Zone 2 Temperature 315-325
Rear-Zone 1 Temperature 310-320
Mold Temperature 150-170
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2008/10/07

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.