PPA UA200A 物性表
添加时间：2012-12-10 15:12LNP LUBRILOY* HIGH TEMPERATURE RESINS COMPOUND
COMBINING TEMPERATURE RESISTANCE WITH LUBRICATION
High temperature LNP Lubriloy compounds provide lubrication at high operating temperatures through a unique, patented lubrication technology.
LNP™ LUBRILOY™ Compound PPA UA200A 塑料物性表
Also known as:LNP™ Lubriloy™ Compound UA-
Product reorder name:UA200A
LNP LUBRILOY* UA200A is a compound based on Poly phthalamide resin containing Aramid Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,break | 880 | kgf/cm² | ASTM D 638 |
| Tensile Strain,break | 3.3 | % | ASTM D 638 |
| Tensile Modulus,50 mm/min | 43800 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 1330 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 37900 | kgf/cm² | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 61 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 3 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2 mm,unannealed | 253 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 118 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 4.50E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 5.93E-05 | 1/℃ | ASTM E 831 |
| Thermal Conductivity | 0.29 | W/m-℃ | ASTM E 1530 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.17 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.42 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.9-1.1 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.4-1.6 | % | ASTM D 955 |
| Wear Factor Washer | 5 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.25 | - | ASTM D 3702 Modified |
| Static COF | 0.21 | - | ASTM D 3702 Modified |
| Source GMD,last updated:2004/09/30 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120-150 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 | % |
| Melt Temperature | 310-315 | ℃ |
| Front-Zone 3 Temperature | 305-315 | ℃ |
| Middle-Zone 2 Temperature | 305-315 | ℃ |
| Rear-Zone 1 Temperature | 305-315 | ℃ |
| Mold Temperature | 120-150 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD, last updated:2004/09/30 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【LNP™ LUBRILOY™ Compound PPA UA200A】