联系我们
塑胶原料报价
- 产 品：PA66 LNP* Lubricomp* Compound RAL22
- 产 地：美国LNP
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
|
Also known as:LNP* Lubricomp* Compound RAL-4022
|
|
Product reorder name:RAL22
|
|
|
|
LNP LUBRICOMP* RAL22 is a compound based on Nylon 66 resin containing PTFE, Aramid. Added features of this material include: Internally Lubricated.
|
|
|
|
Property
|
|
|
|
TYPICAL PROPERTIES (1)
|
||||
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
|
Tensile Stress, break
|
830
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Strain, break
|
8.1
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
35100
|
kgf/cm²
|
ASTM D 638
|
|
|
Flexural Stress
|
1150
|
kgf/cm²
|
ASTM D 790
|
|
|
Flexural Modulus
|
30200
|
kgf/cm²
|
ASTM D 790
|
|
|
Tensile Stress, break
|
79
|
MPa
|
ISO 527
|
|
|
Tensile Strain, break
|
9.5
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
3500
|
MPa
|
ISO 527
|
|
|
Flexural Stress
|
117
|
MPa
|
ISO 178
|
|
|
Flexural Modulus
|
3500
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
|
Izod Impact, unnotched, 23°C
|
75
|
cm-kgf/cm
|
ASTM D 4812
|
|
|
Izod Impact, notched, 23°C
|
13
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Energy @ peak, 23°C
|
65
|
cm-kgf
|
ASTM D 3763
|
|
|
Multiaxial Impact
|
14
|
cm-kgf
|
ISO 6603
|
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
48
|
kJ/m²
|
ISO 180/1U
|
|
|
Izod Impact, notched 80*10*4 +23°C
|
5
|
kJ/m²
|
ISO 180/1A
|
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
248
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
198
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
7.2E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
8.1E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, flow
|
7.36E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, -40°C to 40°C, xflow
|
8.26E-05
|
1/°C
|
ISO 11359-2
|
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
193
|
°C
|
ISO 75/Af
|
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
|
Density
|
1.22
|
g/cm³
|
ASTM D 792
|
|
|
Moisture Absorption, 50% RH, 24 hrs
|
0.72
|
%
|
ASTM D 570
|
|
|
Mold Shrinkage, flow, 24 hrs (5)
|
1.9
|
%
|
ASTM D 955
|
|
|
Mold Shrinkage, xflow, 24 hrs (5)
|
2
|
%
|
ASTM D 955
|
|
|
Mold Shrinkage, flow, 24 hrs (5)
|
1.92
|
%
|
ISO 294
|
|
|
Mold Shrinkage, xflow, 24 hrs (5)
|
1.95
|
%
|
ISO 294
|
|
|
Wear Factor Washer
|
13
|
10^-10 in^5-min/ft-lb-hr
|
ASTM D 3702 Modified
|
|
|
Dynamic COF
|
0.54
|
-
|
ASTM D 3702 Modified
|
|
|
Static COF
|
0.45
|
-
|
ASTM D 3702 Modified
|
|
|
Density
|
1.22
|
g/cm³
|
ISO 1183
|
|
|
Moisture Absorption (23°C / 50% RH)
|
1.17
|
%
|
ISO 62
|
|
|
Source GMD, last updated:2004/09/30
|
|
Processing
|
|
Parameter
|
||
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
80
|
°C
|
|
Drying Time
|
4
|
hrs
|
|
Maximum Moisture Content
|
0.15 - 0.25
|
%
|
|
Melt Temperature
|
275 - 290
|
°C
|
|
Front - Zone 3 Temperature
|
295 - 305
|
°C
|
|
Middle - Zone 2 Temperature
|
280 - 295
|
°C
|
|
Rear - Zone 1 Temperature
|
265 - 275
|
°C
|
|
Mold Temperature
|
80 - 95
|
°C
|
|
Back Pressure
|
0.2 - 0.3
|
MPa
|
|
Screw Speed
|
30 - 60
|
rpm
|
|
Source GMD, last updated:2004/09/30
|