- 产 品:PA66 LNP* Lubricomp* Compound RAL23S
- 产 地:美国LNP
- 价 格:电话报价
- 库 存:20吨
- 交 货:江苏苏州
- 苏州希普能:185 5121 3137 谭经理
Also known as:LNP* Lubricomp* Compound RAL-4023 HS
|
Product reorder name:RAL23S
|
|
LNP LUBRICOMP* RAL23S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Heat Stabilized.
|
|
Property
|
|
TYPICAL PROPERTIES (1)
|
||||
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, break
|
910
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Strain, break
|
5.9
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min
|
37500
|
kgf/cm²
|
ASTM D 638
|
|
Flexural Stress
|
1330
|
kgf/cm²
|
ASTM D 790
|
|
Flexural Modulus
|
40100
|
kgf/cm²
|
ASTM D 790
|
|
Tensile Stress, break
|
85
|
MPa
|
ISO 527
|
|
Tensile Strain, break
|
6.3
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
3800
|
MPa
|
ISO 527
|
|
Flexural Stress
|
107
|
MPa
|
ISO 178
|
|
Flexural Modulus
|
3500
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, unnotched, 23°C
|
54
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
4
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
37
|
kJ/m²
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*4 +23°C
|
4
|
kJ/m²
|
ISO 180/1A
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
171
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
6.66E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
9.72E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, flow
|
6.8E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
9.8E-05
|
1/°C
|
ISO 11359-2
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
246
|
°C
|
ISO 75/Bf
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
160
|
°C
|
ISO 75/Af
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Density
|
1.24
|
g/cm³
|
ASTM D 792
|
|
Mold Shrinkage, flow, 24 hrs (5)
|
1.7 - 1.8
|
%
|
ASTM D 955
|
|
Mold Shrinkage, xflow, 24 hrs (5)
|
2 - 2.1
|
%
|
ASTM D 955
|
|
Wear Factor Washer
|
23
|
10^-10 in^5-min/ft-lb-hr
|
ASTM D 3702 Modified
|
|
Dynamic COF
|
0.38
|
-
|
ASTM D 3702 Modified
|
|
Static COF
|
0.32
|
-
|
ASTM D 3702 Modified
|
|
Density
|
1.23
|
g/cm³
|
ISO 1183
|
|
Source GMD, last updated:2004/09/30
|
Processing
|
Parameter
|
||
Injection Molding
|
Value
|
Unit
|
Drying Temperature
|
80
|
°C
|
Drying Time
|
4
|
hrs
|
Maximum Moisture Content
|
0.15 - 0.25
|
%
|
Melt Temperature
|
275 - 290
|
°C
|
Front - Zone 3 Temperature
|
295 - 305
|
°C
|
Middle - Zone 2 Temperature
|
280 - 295
|
°C
|
Rear - Zone 1 Temperature
|
265 - 275
|
°C
|
Mold Temperature
|
80 - 95
|
°C
|
Back Pressure
|
0.2 - 0.3
|
MPa
|
Screw Speed
|
30 - 60
|
rpm
|
Source GMD, last updated:2004/09/30
|