- 产 品:PA66/PA6 74G33W NC010 玻纤33%增强,耐候
- 产 地:DuPont 杜邦
- 价 格:电话报价
- 库 存:20吨
- 交 货:江苏苏州
- 苏州希普能:185 5121 3137 谭经理
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
UV Resistant/Weatherable Resins
防紫外线/耐候性树脂
Zytel® 74G33W NC010 is a 33% glass reinforced nylon 66 and nylon 6 co-melt resin with improved weatherability.
zytel®74G33W NC01033%玻璃纤维增强尼龙66和尼龙6的合作融化改善耐候性树脂。
Property
|
Test Method
|
Units
|
Value
|
DAM
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66+PA6-GF33
>PA66+PA6-GF33<
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 179/1eA
|
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
|
194(28.1)
4.1
10900(1580)
12.3
16.2
|
Thermal
Deflection Temperature
1.80MPa
|
ISO 75-1/-2
|
℃(℉)
|
225(437)
|
Other
Density
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 294-4
|
3 3
kg/m(g/cm )
%
|
1390(1.39)
0.9
0.3
|
Property
|
Test Method
|
Units
|
Value
|
DAM
|
|||
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
|
280-300(535-570)
290(555)
70-120(160-250)
100(210)
2-4
80(175)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The above data are preliminary and are subject to change as additional data are developed on subsequent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2010