PBT 310SE0 非增强型,PBT阻燃树脂
  • 产 品:PBT 310SE0 非增强型,PBT阻燃树脂
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT 310SE0 数据表
VALOX 310SE0 is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard, switches and switch components and appliance housings.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 590 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 590 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 20 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 20 % ASTM D 638
Tensile Modulus,5mm/min 28700 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 1020 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 26700 kgf/cm² ASTM D 790
Taber Abrasion,CS-17,1 kg 19 mg/1000cy SABIC Method
Tensile Stress,yield,50mm/min 55 MPa ISO 527
Tensile Stress,break,50mm/min 40 MPa ISO 527
Tensile Strain,yield,50mm/min 6 % ISO 527
Tensile Strain,break,50mm/min 20 % ISO 527
Tensile Modulus,1mm/min 2800 MPa ISO 527
Flexural Stress,yield,2mm/min 90 MPa ISO 178
Flexural Modulus,2mm/min 2600 MPa ISO 178
Hardness,H358/30 105 MPa ISO 2039-1
Hardness,Rockwell R 120 - ISO 2039-2
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 163 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 2 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 2039 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 3 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 8 kJ/m² ISO 179/1eA
Charpy Impact,notched,23℃ 4 kJ/m² ISO 179/2C
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 4 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 165 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 74 ASTM D 648
HDT,0.45 MPa,6.4mm,unannealed 162 ASTM D 648
HDT,1.82 MPa,6.4mm,unannealed 71 ASTM D 648
CTE,-40℃ to 40℃,flow 7.92E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.92E-05 1/℃ ASTM E 831
CTE,60℃ to 138℃,flow 1.31E-04 1/℃ ASTM E 831
Thermal Conductivity 0.24 W/m-℃ ISO 8302
CTE,-40℃ to 40℃,flow 7.60E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 7.30E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,flow 1.00E-04 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 1.00E-04 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 212 ISO 306
Vicat Softening Temp,Rate B/50 165 ISO 306
Vicat Softening Temp,Rate B/120 165 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 135 ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 60 ISO 75/Ae
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 71 ISO 75/Af
Relative Temp Index,Elec 120 UL 746B
Relative Temp Index,Mech w/impact 120 UL 746B
Relative Temp Index,Mech w/o impact 140 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.4 - ASTM D 792
Specific Volume 0.71 cm³/g ASTM D 792
Mold Shrinkage on Tensile Bar,flow(2)(5) 1.1-1.8 % SABIC Method
Mold Shrinkage,flow,3.2mm(5) 1.5-2.3 % SABIC Method
Mold Shrinkage,flow,0.75-2.3mm(5) 0.9-1.6 % SABIC Method
Mold Shrinkage,flow,2.3-4.6mm(5) 1.5-2.3 % SABIC Method
Mold Shrinkage on Tensile Bar,xflow(2)(5) 0.9-1.9 % SABIC Method
Mold Shrinkage,xflow,0.75-2.3mm(5) 1-1.7 % SABIC Method
Mold Shrinkage,xflow,2.3-4.6mm(5) 1.6-2.4 % SABIC Method
Melt Flow Rate,250℃/2.16 kgf 8.6 g/10 min ASTM D 1238
Density 1.4 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.36 % ISO 62
Moisture Absorption(23℃ / 50% RH) 0.08 % ISO 62
Melt Volume Rate,MVR at 250℃/2.16 kg 8 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Dielectric Strength,in air,3.2mm 18.4 kV/mm ASTM D 149
Dielectric Strength,in oil,1.6mm 22 kV/mm ASTM D 149
Arc Resistance,Tungsten{PLC} 6 PLC Code ASTM D 495
Hot Wire Ignition{PLC) 2 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 4 PLC Code UL 746A
High Voltage Arc Resistance{PLC) 6 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 0 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 3 PLC Code UL 746A
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,shorttime,1.0mm 18 kV/mm IEC 60243-1
Dielectric Strength,in oil,0.8mm 31 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6mm 24 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2mm 15 kV/mm IEC 60243-1
Relative Permittivity,100 Hz 3.1 - IEC 60250
Relative Permittivity,1 MHz 2.8 - IEC 60250
Dissipation Factor,50/60 Hz 0.001 - IEC 60250
Dissipation Factor,100 Hz 0.002 - IEC 60250
Dissipation Factor,1 MHz 0.01 - IEC 60250
Comparative Tracking Index 175 V IEC 60112
Comparative Tracking Index,M 100 V IEC 60112
Relative Permittivity,50/60 Hz 2.9 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-0 Flame Class Rating(3) 0.71 mm UL 94
UL Recognized,94-5VA Rating(3) 3 mm UL 94
Glow Wire Flammability Index 960℃,passes at 1 mm IEC 60695-2-12
Oxygen Index(LOI) 30 % ISO 4589
Source GMD,last updated:2007/07/27
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 245-260
Nozzle Temperature 240-255
Front-Zone 3 Temperature 245-260
Middle-Zone 2 Temperature 240-255
Rear-Zone 1 Temperature 230-250
Mold Temperature 50-75
Back Pressure 0.3-0.7 MPa
Screw Speed 50-100 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.013-0.025 mm
Source GMD,last updated:2007/07/27

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.