PA66 RFL16 含玻璃纤维,聚四氟乙烯,内部润滑
  • 产 品:PA66 RFL16 含玻璃纤维,聚四氟乙烯,内部润滑
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP Lubricomp* Polyamides Compound
Enhanced wear resistance, lower friction in tough
Polyamide-based LNP Lubricomp compounds provide these tough resins with improved wear resistance and lower friction by combining them with internal lubricants. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound PA66 RFL16 塑料物性

Also known as:LNP™ Lubricomp™ Compound RFL-4016
Product reorder name:RFL16
LNP LUBRICOMP* RFL16 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 1920 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.7 % ASTM D 638
Tensile Modulus,50mm/min 112300 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 2680 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 90900 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 188 MPa ISO 527
Tensile Stress,break,5mm/min 185 MPa ISO 527
Tensile Strain,yield,5mm/min 2.8 % ISO 527
Tensile Strain,break,5mm/min 2.7 % ISO 527
Tensile Modulus,1mm/min 10630 MPa ISO 527
Flexural Modulus,2mm/min 8980 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 115 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 12 cm-kgf/cm ASTM D 256
Multiaxial Impact 23 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 95 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 62 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 10 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 259 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 249 ASTM D 648
CTE,-30℃ to 30℃,flow 3.95E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 9.17E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 262 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 251 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.4 - ASTM D 792
Density 1.43 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.57 % ASTM D 570
Wear Factor Washer 16 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Wear Factor Ring 0 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.55 - ASTM D 3702 Modified
Static COF 0.53 - ASTM D 3702 Modified
Density 1.4 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.88 % ISO 62
Source GMD,last updated:2009/07/06
Parameter Injection Molding Value Unit 
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2009/07/06

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ Lubricomp™ Compound PA66 RFL16