- 产 品：PA66 RL002 含聚四氟乙烯,内部润滑
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP Lubricomp* Polyamides Compound
Enhanced wear resistance, lower friction in tough
Polyamide-based LNP Lubricomp compounds provide these tough resins with improved wear resistance and lower friction by combining them with internal lubricants. Glass and carbon fibers can also be included for improved strength and stiffness.
LNP™ Lubricomp™ Compound PA66 RL002 塑料数据
Also known as:LNP™ Lubricomp™ Compound RL-4020
Product reorder name:RL002
LNP LUBRICOMP* RL002 is a compound based on Nylon 66 resin containing PTFE. Added features of this material include: Internally Lubricated.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield | 760 | kgf/cm² | ASTM D 638 |
| Tensile Stress,break | 760 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yield | 13.5 | % | ASTM D 638 |
| Tensile Strain,break | 14.3 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 31400 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 1140 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 31000 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield | 73 | MPa | ISO 527 |
| Tensile Stress,break | 73 | MPa | ISO 527 |
| Tensile Strain,yield | 16.7 | % | ISO 527 |
| Tensile Strain,break | 17.6 | % | ISO 527 |
| Tensile Modulus,1mm/min | 3170 | MPa | ISO 527 |
| Flexural Stress | 89 | MPa | ISO 178 |
| Flexural Modulus | 2840 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 91 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 3 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 36 | cm-kgf | ASTM D 3763 |
| Multiaxial Impact | 42 | cm-kgf | ISO 6603 |
| Izod Impact,unnotched 80*10*4 +23℃ | 59 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 76 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 8.26E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 8.58E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 8.25E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 8.57E-05 | 1/℃ | ISO 11359-2 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 74 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.19 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.94 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 2.2 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 2.6 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 2.23 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 2.59 | % | ISO 294 |
| Wear Factor Washer | 49 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.27 | - | ASTM D 3702 Modified |
| Static COF | 0.23 | - | ASTM D 3702 Modified |
| Moisture Absorption(23℃/50% RH) | 1.18 | % | ISO 62 |
| Source GMD,last updated:2004/09/30 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15-0.25 | % |
| Melt Temperature | 275-290 | ℃ |
| Front-Zone 3 Temperature | 295-305 | ℃ |
| Middle-Zone 2 Temperature | 280-295 | ℃ |
| Rear-Zone 1 Temperature | 265-275 | ℃ |
| Mold Temperature | 80-95 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2004/09/30 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【LNP™ Lubricomp™ Compound PA66 RL002】