LNP LUBRILOY* POLYAMIDES COMPOUND
TOUGH & STRONG -- WITH UNIQUE LUBRICITY
Polyamide-based LNP Lubriloy compounds provide enhanced lubrication through a unique, patented lubrication technology.

LNP™ LUBRILOY™ Compound PA66 RX05497 塑料物性表

Also known as:LNP™ Lubriloy™ Compound RW
Product reorder name:RX05497
LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,yield 840 kgf/cm² ASTM D 638
Tensile Stress,break 680 kgf/cm² ASTM D 638
Tensile Strain,yield 5.2 % ASTM D 638
Tensile Strain,break 24.4 % ASTM D 638
Tensile Modulus,50mm/min 31000 kgf/cm² ASTM D 638
Flexural Stress 1070 kgf/cm² ASTM D 790
Flexural Modulus 28500 kgf/cm² ASTM D 790
Tensile Stress,yield 69 MPa ISO 527
Tensile Stress,break 57 MPa ISO 527
Tensile Strain,yield 17.2 % ISO 527
Tensile Strain,break 31.4 % ISO 527
Tensile Modulus,1mm/min 2730 MPa ISO 527
Flexural Stress 90 MPa ISO 178
Flexural Modulus 2430 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ NB cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 6 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 612 cm-kgf ASTM D 3763
Multiaxial Impact 776 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 137 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 6 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 58 ASTM D 648
CTE,-40℃ to 40℃,flow 9.86E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 9.12E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 9.86E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 9.13E-05 1/℃ ISO 11359-2
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 58 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.12 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.88 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 2.3-2.5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 2.3-2.5 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 2.31-2.52 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 2.31-2.52 % ISO 294
Wear Factor Washer 10 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.3 - ASTM D 3702 Modified
Static COF 0.16 - ASTM D 3702 Modified
Density 1.12 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 1.18 % ISO 62
Source GMD,last updated:2004/09/30
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/09/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.