LNP STAT-KON* POLYAMIDES COMPOUND
TOUGH, TAILORED ELECTRICAL PROPERTIES
Polyamide-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PA66 RE004 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound RC-1004
Product reorder name:RE004
LNP* Stat-kon* RE004 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,break | 2230 | kgf/cm² | ASTM D 638 |
Tensile Strain,break | 4.3 | % | ASTM D 638 |
Flexural Stress | 3180 | kgf/cm² | ASTM D 790 |
Flexural Modulus | 125800 | kgf/cm² | ASTM D 790 |
Tensile Stress,break | 233 | MPa | ISO 527 |
Tensile Strain,break | 2.9 | % | ISO 527 |
Flexural Stress | 337 | MPa | ISO 178 |
Flexural Modulus | 14600 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 53 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 6 | cm-kgf/cm | ASTM D 256 |
Izod Impact,unnotched 80*10*4 +23℃ | 54 | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 8 | kJ/m² | ISO 180/1A |
PHYSICAL | Value | Unit | Standard |
Density | 1.25 | g/cm³ | ASTM D 792 |
ELECTRICAL | Value | Unit | Standard |
Surface Resistivity | 1.E+02-1.E+06 | Ohm | ASTM D 257 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Compliant,94HB Flame Class Rating(3)(4) | 1.5 | mm | UL 94 by SABIC-IP |
Source GMD,last updated:2004/10/01 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 80 | ℃ |
Drying Time | 4 | hrs |
Maximum Moisture Content | 0.15-0.25 | % |
Melt Temperature | 280-305 | ℃ |
Front-Zone 3 Temperature | 295-305 | ℃ |
Middle-Zone 2 Temperature | 280-295 | ℃ |
Rear-Zone 1 Temperature | 265-275 | ℃ |
Mold Temperature | 95-110 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Source GMD,last updated:2004/10/01 |