快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PBT LW9030FR NC010 玻纤30增强,阻燃级
- 产 地：DuPont 杜邦
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
DuPont Crastin® PBT
熱塑性聚酯樹脂
CRASTIN®LW9030FR NC010 是30％玻璃纤维增强，阻燃聚对苯二甲酸丁二酯合金注塑成型。它改善了表面美观，优良的尺寸稳定性和低翘曲的特点
Crastin® LW9030FR NC010 is a 30% glass fiber reinforced, flame retardant polybutylene terephthalate alloy for injection molding. It has improved surface aesthetics, excellent dimensional stability and low warpage characteristics
| 特性 Property |
测试方法 Test Method |
单位 Units |
数值 Value |
|
| 鉴定 Identification |
树脂鉴定 Resin Identification |
ISO 1043 | - | PBT+ASA-GF30FR(17) |
| 部件标记代码 Part Marking Code |
ISO 11469 | - | >PBT+ASA-GF30FR(17)< | |
| 机械 Mechanical |
断裂应力 Stress at Break |
ISO 527 | MPa (kpsi) | 125(18.1) |
| 断裂伸长率 Strain at Break |
ISO 527 | % | 1.8 | |
| 拉伸模量 Tensile Modulus |
ISO 527 | MPa (kpsi) | 10500(1520) | |
| 拉伸蠕变模量 Tensile Creep Modulus |
ISO 899 | MPa (kpsi) | - | |
| 1h | 9500(1380) | |||
| 1000h | 7400(1070) | |||
| 抗弯强度 Flexural Strength |
ISO 178 | MPa (kpsi) | 175(24.7) | |
| 缺口冲击强度 Notched Charpy Impact Strength |
ISO 179/1eA | kJ/m2 | - | |
| -30°C (-22°F) | 8 | |||
| 23°C (73°F) | 8 | |||
| 无缺口简支梁冲击强度 Unnotched Charpy Impact Strength |
ISO 179/1eU | kJ/m2 | - | |
| -30°C (-22°F) | 40 | |||
| 23°C (73°F) | 40 | |||
| 热 Thermal |
变形温度 Deflection Temperature |
ISO 75-1/-2 | ℃(℉) | - |
| 0.45MPa | 220(428) | |||
| 1.80MPa | 190(374) | |||
| 8.00MPa | 106(223) | |||
| 熔融温度 Melting Temperature |
ISO 11357-1/-3 | ℃(℉) | - | |
| 10°C/min | 225(437) | |||
| 线性热膨胀系数，正常 CLTE, Normal |
ISO 11359-1/-2 | E-4/C (E-4/F) | - | |
| 23 - 55°C (73 - 130°F) | 0.8(0.44) | |||
| 线性热膨胀系数，并行 CLTE, Parallel |
ISO 11359-1/-2 | E-4/C (E-4/F) | - | |
| 23 - 55°C (73 - 130°F) | 0.25 (0.14) | |||
| 热传导率 Thermal Conductivity |
DIN 51046 | W/m K(Btu in/h ft2 F) | 0.26 (1.8) | |
| 维卡软化温度 Vicat Softening Temperature |
ISO 306 | ℃(℉) | - | |
| 10N | 215(419) | |||
| 50N | 150(302) | |||
| 热球压测试 Hot Ball Pressure Test |
VDE 0470 | ℃(℉) | - | |
| Plate 3mm | 180(355) | |||
| 流变 Rheological |
熔体体积流动速率 Melt Volume-Flow Rate |
ISO 1133 | cm3/10min(ml/10min) | 10 |
| 电气 Electrical |
表面电阻 Surface Resistivity |
IEC 60093 | ohm | 1E14 |
| 相对介电常数 Relative Permittivity |
IEC 60250 | - | - | |
| 1E2 Hz | 3.8 | |||
| 1E6 Hz | 3.6 | |||
| 体积电阻率 Volume Resistivity |
IEC 60093 | ohm m | >1E13 | |
| 耗散因数 Dissipation Factor |
IEC 60250 | E-4 | - | |
| 1E2 Hz | 30 | |||
| 1E6 Hz | 150 | |||
| 电气强度 Electric Strength |
IEC 60243-1 | kV/mm (V/mil) | - | |
| 1.0mm | 28 (710) | |||
| 20s, Plate 2mm | 20 (508) | |||
| 电解腐蚀 Electrolytical Corrosion |
IEC 60426 | - | - | |
| Plate 4mm | A1.2 | |||
| CTI | IEC 60112 | V | 375 | |
| CTI | UL 746A | V | 300 | |
| CTI M | IEC 60112 | V | - | |
| Plate 4mm | 175 M | |||
| 易燃 Flammability |
可燃性分类 0.75mm Flammability Classification 0.75mm |
IEC 60695-11-10 | - | V-0 |
| 可燃性分类 0.75mm Flammability Classification 0.75mm |
UL94 | - | V-0 | |
| 5V Rating | IEC 60695-11-20 | - | 5VA | |
| 5V Min. Thickness Tested | IEC 60695-11-20 | mm | 3.0 | |
| 氧指数 Oxygen Index |
ISO 4589-1/-2 | % | 27 | |
| 灼热丝燃烧指数 3.0mm Glow Wire Flammability Index 3.0mm |
IEC 60695-2-12 | ℃ | 960 | |
| 高电流电弧点火电阻 High Amperage Arc Ignition Resistance |
UL 746A | arcs | - | |
| 1.5mm | 38 | |||
| 3.0mm | 18 | |||
| 6.0mm | 18 | |||
| 热丝引燃 Hot Wire Ignition |
UL 746A | s | - | |
| 1.5mm | 36 | |||
| 3.0mm | 69 | |||
| 6.0mm | 144 | |||
| 温度指数 Temperature Index |
RTI, Electrical | UL 746B | ℃ | - |
| 0.75mm | 140 | |||
| RTI, Impact | UL 746B | ℃ | - | |
| 0.75mm | 125 | |||
| 1.5mm | 125 | |||
| 3.0mm | 130 | |||
| RTI, Strength | UL 746B | ℃ | - | |
| 0.75mm | 130 | |||
| 1.5mm | 130 | |||
| 3.0mm | 140 | |||
| 温度指数,拉伸强度 Temperature Index, Tensile Strength |
IEC 60216 | ℃(℉) | - | |
| 20000h | 145(293) | |||
| 5000h | 160(320) | |||
| 其他 Other |
密度 Density |
ISO 1183 | kg/m3 (g/cm3) | 1570 (1.57) |
| 球压痕硬度 H 961/30 Ball Indentation Hardness H 961/30 |
ISO 2039-1 | MPa (kpsi) | 170 (25) | |
| 吸水率 Water Absorption |
ISO 62,Similar to | % | - | |
| 平衡相对湿度50% Equilibrium 50%RH |
0.21 | |||
| 饱和度,浸泡 Saturation,immersed |
0.72 | |||
| 成型收缩率 Molding Shrinkage |
ISO 294-4 | % | - | |
| 正常,2.0毫米 Normal,2.0mm |
0.75 | |||
| 并行,2.0毫米 Parallel,2.0mm |
0.3 | |||
| 处理 Processing |
熔体温度范围 Melt Temperature Range |
- | ℃(℉) | 240-260(465-500) |
| 熔体温度优化 Melt Temperature Optimum |
℃(℉) | 250 (480) | ||
| 模具温度范围 Mold Temperature Range |
℃(℉) | 30-130 (85-265) | ||
| 模具温度优化 Mold Temperature Optimum |
℃(℉) | 80 (175) | ||
| 干燥时间,除湿干燥机 Drying Time, Dehumidified Dryer |
h | 2-4 | ||
| 干燥温度 Drying Temperature |
℃(℉) | 110-130 (230-265) | ||
| PBT处理水分含量 Processing Moisture Content |
% | <0.04 | ||
| 蛇流 Snake Flow |
mm (in) | - | ||
| 100MPa,7×2mm | 380(15) | |||
| 90MPa,5×0.30mm | 10(0.4) | |||
| 90MPa,5×0.50mm | 36(1.4) | |||
| 90MPa,5×0.75mm | 70(2.8) | |||
| 90MPa,5×1.00mm | 107(4.2) | |||