DuPont™ Crastin® PBT
thermoplastic polyester resin
低翘曲树脂
Crastin ® LW9030 NC010 is a 30% glass fiber reinforced polybutylene terephthalate alloy for injection molding. Ithas improved surface aesthetics, excellent dimensional stability and low warpage characteristics.
Property
|
Test Method
|
Units
|
Value
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PBT+ASA-GF30
>PBT+ASA-GF30<
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 899
ISO 178
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
130 (18.9)
2.5
9500 (1380)
9000 (1300)
7300 (1606)
8500 (1230)
190 (27.6)
9
10
65
60
|
Property
|
Test Method
|
Units
|
Value
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
8.00MPa
Melting Temperature
10°C/min
CLTE, Normal
23 - 55°C (73 - 130°F)
CLTE, Parallel
23 - 55°C (73 - 130°F)
Thermal Conductivity
Vicat Softening Temperature
10N
50N
Hot Ball Pressure Test
Plate 3mm
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
DIN 51046
ISO 306
VDE 0470
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
2
W/m K (Btu in/h ft F)
°C (°F)
°C
|
215 (419)
175 (347)
97 (207)
225 (437)
1.0 (0.56)
0.25 (0.14)
0.26 (1.8)
214 (417)
150 (302)
180
|
Electrical
Surface Resistivity
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
Dissipation Factor
1E2 Hz
1E6 Hz
Electric Strength
1.0mm
20s, Plate 2mm
|
IEC 60093
IEC 60250
IEC 60093
IEC 60250
IEC 60243-1
|
ohm
ohm m
E-4
kV/mm
|
1E14
3.8
3.6
>1E13
30
170
36
21
|
Property
|
Test Method
|
Units
|
Value
|
Electrical
Electrolytical Corrosion
Plate 4mm
CTI
CTI
3.0mm
CTI M
Plate 4mm
|
IEC 60426
IEC 60112
UL 746A
IEC 60112
|
V
V
|
A1
550
500
175 M
|
Flammability
Flammability Classification
1.5mm
Flammability Classification
1.5mm
Oxygen Index
Glow Wire Flammability Index
3.0mm
High Amperage Arc Ignition Resistance
1.5mm
3.0mm
6.0mm
Hot Wire Ignition
1.5mm
3.0mm
6.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
IEC 60695-2-1
UL 746A
UL 746A
|
%
°C
arcs
s
|
HB
HB
19
650
25
26
17
34
132
150
|
Property
|
Test Method
|
Units
|
Value
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
1.5mm
3.0mm
RTI, Strength
0.75mm
Temperature Index, Tensile Strength
20000h
5000h
|
UL 746B
UL 746B
UL 746B
IEC 60216
|
°C
°C
°C
°C (°F)
|
130
125
125
130
130
145 (293)
160 (320)
|
Other
Density
Ball Indention Hardness
H 961/30
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039-1
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
MPa (kpsi)
%
%
|
1440 (1.44)
175 (25)
0.24
0.72
0.65
0.25
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
|
240-260 (465-500)
250 (480)
30-130 (85-265)
80 (175)
|
Property
|
Test Method
|
Units
|
Value
|
Processing
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Snake Flow
100MPa, 7 x 2mm
90MPa, 5x0.30mm
90MPa, 5x0.50mm
90MPa, 5x0.75mm
90MPa, 5x1.00mm
|
|
h
°C (°F)
%
mm
|
2-4
110-130 (230-265)
<0.04
400
11
38
70
110
|