杜邦™CRASTIN®PBT
热塑性聚酯树脂
非增强树脂
Crastin® S600F40 NC010 is an unreinforced, lubricated, low viscosity polybutylene terephthalate resin for injection molding.
CRASTIN®S600F40 NC010 非增强型,润滑,低粘度聚对苯二甲酸丁二酯树脂注塑。
Property
|
Test Method
|
Units
|
Value
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PBT
>PBT<
|
Mechanical
Yield Stress
Yield Strain
Strain at Break
50mm/min
Nominal Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 899
ISO 178
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
%
%
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
58 (8.4)
6
>50
30
2600 (377)
2600 (377)
1800 (260)
2400 (341)
85 (12.3)
4
4
N
N
|
Property
|
Test Method
|
Units
|
Value
|
Thermal
Deflection Temperature
0.45MPa
0.45MPa, Annealed
1.80MPa
1.80MPa, Annealed
Melting Temperature
10°C/min
CLTE, Parallel
23 - 55°C (73 - 130°F)
CLTE, Normal
23 - 55°C (73 - 130°F)
Glass Transition Temperature
10°C/min
Thermal Conductivity
Thermal Conductivity
Specific Heat
Vicat Softening Temperature
10N, 50°C/h
50N, 50°C/h
Hot Ball Pressure Test
Plate 3mm
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 11357-1/-2
DIN 51046
ISO 11357-4
ISO 306
IEC 60309
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
°C (°F)
2
W/m K (Btu in/h ft F)
2
W/m K (Btu in/h ft F)
J/kg K (Btu/lb F)
°C (°F)
°C (°F)
|
115 (239)
180 (356)
50 (122)
60 (140)
225 (437)
1.1 (0.61)
1.2 (0.67)
55 (131)
0.21 (1.5)
0.25 (0.95)
2110 (0.5)
215 (420)
175 (350)
180 (355)
|
Rheological
Melt Volume-Flow Rate
|
ISO 1133
|
3
cm /10 min (ml/10 min)
|
32
|
Property
|
Test Method
|
Units
|
Value
|
Electrical
Surface Resistivity
Volume Resistivity
Electric Strength
1.0mm
2.0mm
Relative Permittivity
1E2 Hz
1E6 Hz
50Hz
Dissipation Factor
1E2 Hz
1E6 Hz
50Hz
Electrolytical Corrosion
Plate 4mm
CTI
CTI
|
IEC 60093
IEC 60093
IEC 60243-1
IEC 60250
IEC 60250
IEC 60426
IEC 60112
UL 746A
|
ohm
ohm m
kV/mm (V/mil)
E-4
V
V
|
>1E12
>1E13
26 (660)
26 (660)
3.8
3.2
3.8
20
200
20
A1
600
250
|
Flammability
Flammability Classification
1.5mm
Flammability Classification
1.5mm
Oxygen Index
Glow Wire Flammability Index
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
IEC 60695-2-12
|
%
°C
|
HB
HB
22
750
|
Property
|
Test Method
|
Units
|
Value
|
Flammability
High Amperage Arc Ignition Resistance
1.5mm
3.0mm
6.0mm
Hot Wire Ignition
1.5mm
3.0mm
6.0mm
|
UL 746A
UL 746A
|
arcs
s
|
60
120
120
15
15
60
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
RTI, Strength
0.75mm
|
UL 746B
UL 746B
UL 746B
|
°C
°C
°C
|
130
115
120
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
%
%
|
1310 (1.31)
0.2
0.4
1.8
1.95
|
Property
|
Test Method
|
Units
|
Value
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
|
240-260 (465-500)
250 (480)
30-130 (85-265)
80 (175)
2-4
110-130 (230-265)
<0.04
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Crastin® are trademarks or registered trademarks of DuPont Company. Copyright© 2010