Cycoloy* Resin PC/ABS C6200
Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
Property
TYPICAL PROPERTIES (1)
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,50mm/min | 680 | kgf/cm² | ASTM D 638 |
Tensile Strain,brk,Type I,50mm/min | 50 | % | ASTM D 638 |
Flexural Stress,yld,2.6mm/min,100mm span | 1050 | kgf/cm² | ASTM D 790 |
Flexural Modulus,2.6mm/min,100mm span | 27400 | kgf/cm² | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact,notched,23℃ | 54 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Energy @ peak,23℃ | 622 | cm-kgf | ASTM D 3763 |
Instrumented Impact Energy @ peak,-30 | 553 | cm-kgf | ASTM D 3763 |
THERMAL | Value | Unit | Standard |
HDT,1.82 MPa,3.2mm,unannealed | 87 | ℃ | ASTM D 648 |
HDT,1.82 MPa,6.4mm,unannealed | 90 | ℃ | ASTM D 648 |
Relative Temp Index,Elec | 85 | ℃ | UL 746B |
Relative Temp Index,Mech w/impact | 85 | ℃ | UL 746B |
Relative Temp Index,Mech w/o impact | 85 | ℃ | UL 746B |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.18 | - | ASTM D 792 |
Mold Shrinkage,flow,3.2mm(5) | 0.4-0.6 | % | SABIC Method |
Mold Shrinkage,xflow,3.2mm(5) | 0.4-0.6 | % | SABIC Method |
Melt Flow Rate,260℃/2.16 kgf | 14.5 | g/10 min | ASTM D 1238 |
Spiral Flow,260℃,10 ips,3.175 X 1524mm | 685.8 | mm | - |
ELECTRICAL | Value | Unit | Standard |
Arc Resistance,Tungsten{PLC} | 6 | PLC Code | ASTM D 495 |
Hot Wire Ignition{PLC) | 2 | PLC Code | UL 746A |
High Voltage Arc Track Rate{PLC} | 3 | PLC Code | UL 746A |
High Ampere Arc Ign,surface{PLC} | 0 | PLC Code | UL 746A |
Comparative Tracking Index(UL){PLC} | 2 | PLC Code | UL 746A |
Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
Surface Resistivity,ROA | >1.E+15 | Ohm | IEC 60093 |
Dielectric Strength,in oil,0.8mm | 35 | kV/mm | IEC 60243-1 |
Dielectric Strength,in oil,1.6mm | 25 | kV/mm | IEC 60243-1 |
Dielectric Strength,in oil,3.2mm | 17 | kV/mm | IEC 60243-1 |
Relative Permittivity,1 MHz | 2.7 | - | IEC 60250 |
Dissipation Factor,50/60 Hz | 0.004 | - | IEC 60250 |
Dissipation Factor,1 MHz | 0.008 | - | IEC 60250 |
Relative Permittivity,50/60 Hz | 2.8 | - | IEC 60250 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized,94HB Flame Class Rating(3) | 0.71 | mm | UL 94 |
UL Recognized,94V-1 Flame Class Rating(3) | 1.21 | mm | UL 94 |
UL Recognized,94V-0 Flame Class Rating(3) | 1.47 | mm | UL 94 |
UL Recognized,94-5VA Rating(3) | 3.4 | mm | UL 94 |
UL Recognized,94-5VB Rating(3) | 2 | mm | UL 94 |
Source GMD,last updated:2000/01/05 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 80-90 | ℃ |
Drying Time | 3-4 | hrs |
Drying Time(Cumulative) | 8 | hrs |
Maximum Moisture Content | 0.04 | % |
Melt Temperature | 245-275 | ℃ |
Nozzle Temperature | 245-275 | ℃ |
Front-Zone 3 Temperature | 245-275 | ℃ |
Middle-Zone 2 Temperature | 220-275 | ℃ |
Rear-Zone 1 Temperature | 220-255 | ℃ |
Mold Temperature | 60-80 | ℃ |
Back Pressure | 0.3-0.7 | MPa |
Screw Speed | 40-70 | rpm |
Shot to Cylinder Size | 30-80 | % |
Vent Depth | 0.038-0.076 | mm |
Source GMD,last updated:2000/01/05 |
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字:【Cycoloy* Resin PC/ABS C6200】