- 产 品：PPO WCV065 无卤FR,PPE+聚烯烃树脂
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Noryl* Flexible Noryl Resin
Flexible and non Halogenated
Flexible materials comprised of PPO™ resin (polyphenylene ether) and TPE's (thermoplastic elastomers) are commonly used for wire, cable and jacket insulation.
Noryl* Resin WCV065 英文物性表
Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 370 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 370 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 37 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 45 | % | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 410 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 11700 | kgf/cm² | ASTM D 790 |
| Hardness,Shore D,30S reading | 65 | - | ASTM D 2240 |
| Tensile Stress,yield,50mm/min | 39 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 37 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 17 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 38 | % | ISO 527 |
| Tensile Modulus,1mm/min | 1450 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 44 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 1260 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 56 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 336 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,-30℃ | 428 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 41 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 9 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 43 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 71 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2mm,unannealed | 115 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 84 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 8.20E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 1.31E-04 | 1/℃ | ASTM E 831 |
| Vicat Softening Temp,Rate B/50 | 71 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 76 | ℃ | ISO 306 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 93 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity ppo | 1.04 | - | ASTM D 792 |
| Melt Flow Rate,280℃/5.0 kgf | 20.2 | g/10 min | ASTM D 1238 |
| Melt Volume Rate,MVR at 280℃/5.0 kg | 20 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Relative Permittivity,1 MHz | 2.5 | - | IEC 60250 |
| Dissipation Factor,1 MHz | 0.002 | - | IEC 60250 |
| Source GMD,last updated:2007/06/21 | |||
| Parameter Wire Coating Extrusion | Value | Unit |
| Drying Temperature | 60-80 | ℃ |
| Drying Time | 4-6 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | - |
| Screw Speed | 15-40 | rpm |
| Feed Zone Temperature | 210-260 | ℃ |
| Middle Zone Temperatures | 230-285 | ℃ |
| Head Zone Temperature | 250-285 | ℃ |
| Neck Temperature | 250-285 | ℃ |
| Cross-head Temperature | 250-285 | ℃ |
| Die Temperature | 250-285 | ℃ |
| Melt Temperature | 250-285 | ℃ |
| Conductor Pre-heat Temperature | 80-150 | ℃ |
| Screen Pack | 150-100 | - |
| Cooling Water Air Gap | 100-200 | mm |
| Water Bath Temperature | 15-80 | ℃ |
| Source GMD,last updated:2007/06/21 | ||
• NOTE: Recommended Drying Parameters are based on usage of Dehumidify Drying / Drying Oven.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、 Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.