快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
- 产 品：PP M1000S 复合聚丙烯树脂,热稳定
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP Colorcomp* Olefins Compound
On-target color for broad-use resins
Olefinic LNP Colorcomp pre-colored unfilled compounds offer colorants and special effects without loss of key properties. Offerings include opaque, translucent, and transparent resins, plus special effects, including edge glow, sparkle, glow, pearlescent, and thermochromic.
LNP™Colorcomp™ Compound PP M1000S 数据
Also known as:LNP™Colorcomp™Compound M-1000 HS
Product reorder name:M1000S
LNP COLORCOMP* M1000S is a compound based on Polypropylene resin containing Unfilled Glow In the Dark Custom Color. Added features of this material include: Heat Stabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield | 28 | MPa | ISO 527 |
| Tensile Stress,break | 26 | MPa | ISO 527 |
| Tensile Strain,yield | 7 | % | ISO 527 |
| Tensile Strain,break | 40 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2160 | MPa | ISO 527 |
| Flexural Stress | 40 | MPa | ISO 178 |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched 80*10*4 +23℃ | 3 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 130 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 94 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.13 | g/cm³ | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 1.5-1.7 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.5-1.7 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 1.51-1.67 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.51-1.67 | % | ISO 294 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Source GMD,last updated:2004/09/28 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Melt Temperature | 215-220 | ℃ |
| Front-Zone 3 Temperature | 205-215 | ℃ |
| Middle-Zone 2 Temperature | 200-210 | ℃ |
| Rear-Zone 1 Temperature | 195-205 | ℃ |
| Mold Temperature | 30-50 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2004/09/28 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.PBT CL100 紫外线稳定,PC+PBT共混物,耐溶剂,耐低温
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【LNP™Colorcomp™ Compound PP M1000S】