DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Toughened Resins
增韧树脂
Zytel® ST801AW NC010 is a Super Tough, high performance polyamide 66 resin. It is UV stabilized and when appropriately colored offers the best resistance to indirect sunlight in automotive interior applications.
zytel的®ST801AW NC010是一个超级强韧,高性能聚酰胺66树脂。它是紫外线稳定和适当的颜色时,提供了最好的抵抗阳光直射在汽车内部应用。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-HI
>PA66-HI<
|
|
Mechanical
Yield Stress
Yield Strain
Stress at Break
50mm/min
Strain at Break
50mm/min
Nominal Strain at Break
Tensile Modulus
Tensile Stress
@ 50% Strain
Flexural Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
-20℃(-4℉)
0℃(32℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
|
MPa(kpsi)
%
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
|
49(7.1)
5
45(6.5)
74
44
1900(276)
50(7.2)
1800(261)
21
23
22
36
83
|
35.5(5.1)
26.5
48(7.0)
>50
775(112)
48(7.0)
728(106)
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Mechanical
Unnotched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
-20℃(-4℉)
0℃(32℉)
23℃(73℉)
|
ISO 179/1eU
|
2
kJ/m
|
240
NB
300
260
NB
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-30-30℃(-22-86℉)
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-30-30℃(-22-86℉)
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
155(311)
60(140)
262(504)
1.1(0.6)
1.1(0.6)
1.2(0.7)
1.2(0.7)
1.3(0.7)
1.2(0.7)
1.4(0.8)
1.7(0.9)
|
|
Electrical
Surface Resistivity
Volume Resistivity
Electric Strength
Relative Permittivity
1E2 Hz
1E6 Hz
|
IEC 60093
IEC 60093
IEC 60243-1
IEC 60250
|
ohm
ohm m
kV/mm(V/mil)
|
2.7E15
2.5E14
26(660)
3.4
3.2
|
7.1E12
2.4E10
26(660)
6.0
3.5
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Electrical
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
|
IEC 60250
UL 746A
|
E-4
V
|
50
110
600
|
1760
380
|
Flammability
Flammability Classification
0.75mm
Flammability Classification
0.75mm
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
150
150
150
19
28
73
|
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
RTI, Strength
0.75mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
125
75
85
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Other
Density
Hardness, Rockwell
Scale R
Water Absorption
Immersion 24h
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1080(1.08)
110
1.17
1.8
2.0
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
270-300(520-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2006.